Dry lubricating films containing solid lubricants

  • Dry film lubricants formulated with solid lubricants, such as molybdenum disulfide(MoS2), PTFE and graphite, and binders. Applied like a coating, they form a lubricating film at room temperature or after being dried by heating.
  • Applicable to diverse parts, such as metals, plastics, and rubbers.
  • Ideal for applications aimed at improving initial running-in, wear resistance, adherence prevention and low friction performance, those involving locations where oil and other normal lubricants cannot be used, and those based on a desire to achieve a synergy effect with such lubricants.
Read moreShow less
Enquire Now
Description
Seizure Prevention
  • Contain solid lubricants such as molybdenum disulfide, known for superior lubricity under heavy loads, in high concentrations.
  • As the film is relatively soft, the coats are excellent in preventing seizure, while quickly providing an ideal lubricating surface during initial running-in lubrication.
Product Name Treatable Material Appearance Binder Curing Conditions Solid Lubricant Additives Remarks
Molydry 1610 Metal Black Epoxy Resin 180℃×30min Molybdenum Disulfide,Graphite Excellent initial running-in and anti-seizure performance.
Molydry 1670 Molybdenum Disulfide Excellent anti-rust and chemical resistance performance and amenability to dipping and tumbling treatment.
Molydry 5511 Inorganic Compound 150℃×30min
（Drying under room temperature permitted）		 Molybdenum Disulfide,Graphite Excellent heat resistance and load bearing performance and amenability to dipping and tumbling treatment.
Low Friction
  • Contain PTFE, known for superior low friction performance.
  • As the film is relatively hard, the coats are ideal for the pursuit of even more enhanced low friction performance and provision of permanent lubrication under low surface pressure.
Product Name Treatable Material Appearance Binder Curing Conditions Solid Lubricant Additives Remarks
Drycoat 2510 Metal White Epoxy Resin 180℃×30min PTFE Excellent durability and low friction.
Drycoat 3500 Black Polyamideimide 230℃×30min Molybdenum Disulfide,PTFE Excellent heat resistance, adherence, and low friction.
Molydry 3712 Epoxy Resin 180℃×30min Hard film and corrosion resistance.
Heat and Wear Resistance
  • Contain solid lubricants, such as molybdenum disulfide, known for superior lubricity under heavy loads, and graphite, known for superior heat resistance, in high concentrations.
  • As the film is relatively hard, the coats have excellent heat resistance and　wear resistance, and are therefore ideal for applications with demanding temperature and load conditions.
Product Name Treatable Material Appearance Binder Curing Conditions Solid Lubricant Additives Remarks
Molydry 1900 Metal Black Polyamideimide 190℃×60min Molybdenum Disulfide,
Graphite		 Excellent heat resistance, durability, and load bearing performance.
Molydry 2810 230℃×30min Excellent heat resistance, load bearing, and initial running-in performance.
Simple Type
  • A dry film that can be cured at a low temperature, dipped, and easily coated.
Product Name Treatable Material Appearance Binder Curing Conditions Solid Lubricant Additives Remarks
Moly C-S Metal, plastic, and rubber Black Cellulose Drying under room temperature Molybdenum Disulfide Amenability to dipping and tumbling treatment.
Other
  • A dry film for oil-less sliding parts.
Product Name Treatable Material Appearance Binder Curing Conditions Solid Lubricant Additives Remarks
Molydry 1711 Metal Black Epoxy Resin 160℃×60min Molybdenum Disulfide For oil-less sliding parts produced by filling preprocessed grooves with paint.
Read moreShow less
More Information
You May Also Like
Related Products
Dry Lubrication Dry Lubrication
SUMICO

Dry Lubrication Spray  Containing solid lubricants (PTFE, Molybdenum Disulfide or Boron Nitride) Easily Produce a Dry Lubricating Film That Reduces Friction and Wear